CW40-705 F0101 Excellent adhesion Suitable for paper products wood processing book printing and packaging

CW40-705 Emulsion is a high-quality universal adhesive featuring excellent initial tack and mechanical stability. Compared to polyvinyl acetate emulsions, its application properties—including curing speed and bonding strength—have been significantly enhanced. It exhibits strong adhesion to plastic films and aluminum foil, provides polymer-based long-term flexibility for paper-based laminates, and offers broad formulation versatility.

Project	Indicator			Typical Performance
Project	Premium Grade		equivalent	/	/
Appearance	White or slightly yellow emulsion, free of coarse particles, foreign matter, and sediment			Mechanical stability	Very good
Residue on evaporation. % ≥	54.5	54.5		Low-temperature stability	Generally
Viscosity. mPa·s (25°C)	1500-2200	1200-2200		dry tackiness	Micro
PH	4.0-6.5	4.0-6.5		wet stickiness	good
Residual VAC.% ≤	1.0	1.0		Boron resistance	Coagulation
Ethylene content.%	14-18	14-18		Water resistance	Generally
Particle size ≤ μm	0.2-2.0	0.2-2.0		Tensile strength.MPa	4.3
Dilution Stability. % ≤	3.5	3.5		Membrane Permeability	Slightly blurred
Film formation temperature.°C ≤	-3	0		Heat seal temperature.°C	82
Note 1: The product complies with the enterprise standard (Q/SHCW 107-2003)
Note 2: The percentage in this table represents mass fraction.

Parameters

Project	Indicator			Typical Performance
Project	Premium Grade		equivalent	/	/
Appearance	White or slightly yellow emulsion, free of coarse particles, foreign matter, and sediment			Mechanical stability	Very good
Residue on evaporation. % ≥	54.5	54.5		Low-temperature stability	Generally
Viscosity. mPa·s (25°C)	1500-2200	1200-2200		dry tackiness	Micro
PH	4.0-6.5	4.0-6.5		wet stickiness	good
Residual VAC.% ≤	1.0	1.0		Boron resistance	Coagulation
Ethylene content.%	14-18	14-18		Water resistance	Generally
Particle size ≤ μm	0.2-2.0	0.2-2.0		Tensile strength.MPa	4.3
Dilution Stability. % ≤	3.5	3.5		Membrane Permeability	Slightly blurred
Film formation temperature.°C ≤	-3	0		Heat seal temperature.°C	82
Note 1: The product complies with the enterprise standard (Q/SHCW 107-2003)
Note 2: The percentage in this table represents mass fraction.